品名： LDPE 牌号：K203 厂家：雪佛龙菲利普斯
规格用途| 规格级别 | 其它 其它 挤出 | 外观颜色 | nan |
| 该料用途 | 覆盖、薄片 | ||
| 备注说明 | 好的加工性能 | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 密度 | nan | ASTM D-1505 | 0.922 | g/cm3 |
| 熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 15 | g/10min | |
| 密度 | nan | ASTM D-1505 | 0.924 | g/cc | |
| 熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 15 | g/10min | |
| 机械性能 | 环境应力开裂 | ConditionA/B,100% lgepal,F50 | ASTM D-1693 | 1500 | hr |
| 屈服拉伸强度 | nan | ASTM D-638 | 12 | MPa | |
| 断裂伸长率 | nan | ASTM D-638 | 750 | % | |
| 弯曲模量 | nan | ASTM D-790 | 480 | MPa | |
| 拉伸冲击强度 | nan | ASTM D-1822 | 800 | kJ/m2 | |
| 邵氏硬度 | nan | ASTM D-2240 | 55 | nan | |
| 环境应力开裂 | 50℃ | ASTM D-1693 | ≥1500 | hour | |
| 屈服拉伸强度 | nan | ASTM D-638 | 13 | MPa | |
| 断裂伸长率 | nan | ASTM D-638 | ≥700 | % | |
| 弯曲模量 | nan | ASTM D-790 | 0.480 | GPa | |
| 热性能 | 热变形温度 | 0.45MPa | ASTM D-648 | 51 | ℃ |
| 脆化温度 | nan | ASTM D-746 | -75 | ℃ | |
| 维卡软化点 | nan | ASTM D-1525 | 104 | ℃ | |
| 加工温度 | nan | nan | 193-232 | ℃ |