规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
玻璃纤维加固 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
24hr |
ASTM D-570 |
0.20 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
0.20 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
0.25 |
% |
| 吸水率 |
24hr |
ASTM D-570 |
0.050 |
% |
| 吸水率 |
24hr,3.18mm |
ASTM D-570 |
0.25 |
% |
| 吸水率 |
24hr,3.18mm |
ASTM D-570 |
0.15 |
% |
| 吸水率 |
24hr,3.18mm |
ASTM D-570 |
0.15 |
% |
| 吸水率 |
24hr,3.18mm |
ASTM D-570 |
0.15 |
% |
| 吸水率 |
24hr,3.18mm |
ASTM D-570 |
0.12 |
% |
| 密度 |
nan |
ASTM D-792 |
1.18 |
nan |
| 吸水率 |
24hr 浸泡 |
ASTM D-570 |
0.01 |
% |
| 热性能 |
热变形温度 |
1.80MPa，退火，3.18mm |
ASTM D-648 |
96.1 |
℃ |
| 热变形温度 |
1.80MPa，退火，3.18mm |
ASTM D-648 |
96.1 |
℃ |
| 燃烧性 |
nan |
UL 94 |
HB |
nan |
| 热变形温度 |
0.45MPa，退火，3.18mm |
ASTM D-648 |
98.9 |
℃ |
| 热变形温度 |
1.80MPa，退火，3.18mm |
ASTM D-648 |
91.1 |
℃ |
| CLTE |
nan |
ASTM D-696 |
0.000036 |
cm/cm℃ |
| 燃烧性 |
nan |
UL 94 |
HB |
nan |
| 热变形温度 |
0.45MPa，退火，6.35mm |
ASTM D-648 |
98.9 |
℃ |
| 热变形温度 |
1.80MPa，退火，6.35mm |
ASTM D-648 |
96.1 |
℃ |
| 热变形温度 |
0.45MPa，未退火,6.35mm |
ASTM D-648 |
107 |
℃ |
| 热变形温度 |
1.80MPa，未退火，6.35mm |
ASTM D-648 |
96.1 |
℃ |
| 热变形温度 |
0.45MPa，未退火,6.35mm |
ASTM D-648 |
102 |
℃ |
| 热变形温度 |
1.80MPa，未退火，6.35mm |
ASTM D-648 |
93.3 |
℃ |
| 热变形温度 |
0.45MPa，未退火，6.35mm |
ASTM D-648 |
85.0 |
℃ |
| 热变形温度 |
1.80MPa，未退火，6.35mm |
ASTM D-648 |
75.0 |
℃ |
| 燃烧性 |
nan |
UL 94 |
HB |
nan |
| 热变形温度 |
0.45MPa，未退火，6.35mm |
ASTM D-648 |
113 |
℃ |
| 热变形温度 |
1.80MPa，未退火，6.35mm |
ASTM D-648 |
98.9 |
℃ |
| 热变形温度 |
1 MPa,0.125 in |
ASTM D-648 |
115 |
MPa |
| 热变形温度 |
nan |
ASTM D-648 |
137 |
℃ |
| 热变形温度 |
nan |
ASTM D-648 |
160 |
℃ |
| 热变形温度 |
0.46MPa |
ASTM D-648 |
135 |
℃ |
| 热变形温度 |
1.8MPa |
ASTM D-648 |
116 |
℃ |
| 热变形温度 |
1.8MPa |
ASTM D-648 |
135 |
℃ |
| 线性热膨胀系数 |
68℉ |
ASTM D-696 |
37.8 |
µm/m-℃ |
| 热变形温度 |
0.46MPa |
ASTM D-648 |
138 |
℃ |
| 热变形温度 |
1.8MPa |
ASTM D-648 |
135 |
℃ |
| 机械性能 |
拉伸模量 |
|
ASTM D638 |
11700 |
MPa |
| 抗张强度 |
断裂 |
ASTM D638 |
62.3 |
MPa |
| 伸长率 |
断裂 |
ASTM D638 |
2.3 |
% |
| 弯曲模量 |
|
ASTM D790 |
7380 |
MPa |
| 弯曲强度 |
|
ASTM D790 |
107 |
MPa |
| 悬臂梁缺口冲击强度 |
23℃，6.35mm,注塑 |
ASTM D256A |
37.4 |
J/m |