规格用途
| 规格级别 |
通用 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
高冲击 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
熔体流动速率 |
nan |
JIS K7210 |
11 |
g/10min |
| 表观密度 |
nan |
ASTM D-1895 |
0.37 |
g/cm3 |
| 熔体质量流动速率 |
230℃/3.8kg |
ASTM D-1238 |
3.7 |
g/10min |
| 比重 |
|
ASTM D792 |
1.05 |
g/cm3 |
| 熔体流动速率 |
230℃/2.16kg |
ASTM D1238 |
4.0 |
g/10min |
| 收缩率 |
流动 |
ASTM D955 |
1.1-1.4 |
% |
| 物理性能 |
密度 |
|
ASTM D792 |
1.14 |
|
| 吸水率 |
24小时，23℃ |
ASTM D570 |
1.5 |
% |
| 收缩率 |
平行流动方向 |
ASTM D955 |
0.014 - 0.018 |
cm/cm |
| 热性能 |
维卡软化点 |
nan |
ASTM D-1525 |
107 |
℃ |
| 热变形温度 |
nan |
ASTM D-648 |
86 |
℃ |
| 热变形温度 |
18.6kg/cm2 |
ASTM D648 |
100 |
℃ |
| 热膨胀系数 |
nan |
ASTM D696 |
7.3×10-5 |
mm/mm/℃ |
| 阻燃性 |
nan |
UL94 |
HB |
nan |
| 热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
124 |
℃ |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D648 |
68.0 |
℃ |
| 线型膨胀系数 |
流动 |
ASTM D696 |
0.000080 |
cm/cm/℃ |