规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 热性能 |
脆化温度 |
|
ASTM D746 |
-70.0 |
°C |
| 维卡软化温度 |
|
ASTM D1525 |
90.0 |
°C |
| 熔融温度 |
|
ASTM D1525 |
102 |
°C |
| 脆化温度 |
|
ASTM D746 |
-70.0 |
°C |
| 维卡软化温度 |
|
ASTM D1525 |
90.0 |
°C |
| 熔融温度 |
|
ASTM D1525 |
102 |
°C |
| 物理性能 |
密度 |
|
ASTM D1505 |
0.928 |
g/cm³ |
| 熔流率 |
190°C/2.16 kg |
ASTM D1238 |
2.5 |
g/10 min |
| 醋酸乙烯含量 |
|
|
6.0 |
wt% |
| 硬度计硬度 |
支撐 A |
ASTM D224 |
47 |
|
| 密度 |
|
ASTM D1505 |
0.928 |
g/cm³ |
| 熔流率 |
190°C/2.16 kg |
ASTM D1238 |
2.5 |
g/10 min |
| 醋酸乙烯含量 |
|
|
6.0 |
wt% |
| 硬度计硬度 |
支撐 A |
ASTM D224 |
47 |
|
| 机械性能 |
抗张强度 |
屈服 |
ASTM D638 |
7.85 |
MPa |
| |
断裂 |
ASTM D638 |
14.7 |
MPa |
| 伸长率 |
断裂 |
ASTM D638 |
700 |
% |
| 弯曲模量 |
|
ASTM D790 |
35.3 |
MPa |
| 薄膜厚度 |
经测试 |
|
30 |
µm |
| 抗张强度 |
屈服 |
ASTM D638 |
7.85 |
MPa |
| |
断裂 |
ASTM D638 |
14.7 |
MPa |
| 伸长率 |
断裂 |
ASTM D638 |
700 |
% |
| 弯曲模量 |
|
ASTM D790 |
35.3 |
MPa |
| 薄膜厚度 |
经测试 |
|
30 |
µm |