品名： LLDPE 牌号：3224 厂家：韩国韩华
规格用途| 规格级别 | 其它 薄膜 挤出 | 外观颜色 | nan |
| 该料用途 | 包装用，农膜，拉伸包装膜。 | ||
| 备注说明 | 加工性,热封合性 | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 热性能 | 脆化温度 | ASTM D746 | -70.0 | °C | |
| 维卡软化温度 | ASTM D1525 | 93.0 | °C | ||
| 熔融温度 | ASTM D1525 | 122 | °C | ||
| 基本性能 | 密度 | nan | ASTM D-1505 | 0.920 | g |
| 熔融指数 | nan | ASTM D-1238 | 2 | g/10分 | |
| 密度 | nan | ASTM D-1505 | 0.920 | g/cc | |
| 熔体流动速率 | ASTM D-1238 | 2.0 | g/10min | ||
| 密度 | ASTM D-1505 | 0.920 | g/cm3 | ||
| 薄膜 | 薄膜厚度 | 经测试 | 38 | µm | |
| 割线模量 | 1% 正割, MD: 38 µm, 吹塑薄膜 | ASTM D882 | 147 | MPa | |
| 1% 正割, TD: 38 µm, 吹塑薄膜 | ASTM D882 | 206 | MPa | ||
| 抗张强度 | MD: 屈服, 38 µm, 吹塑薄膜 | ASTM D882 | 9.81 | MPa | |
| TD: 屈服, 38 µm, 吹塑薄膜 | ASTM D882 | 10.8 | MPa | ||
| MD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 35.3 | MPa | ||
| TD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 27.5 | MPa | ||
| 伸长率 | MD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 600 | % | |
| TD: 断裂, 38 µm, 吹塑薄膜 | ASTM D882 | 800 | % | ||
| 落锤冲击 | 38 µm, 吹塑薄膜 | ASTM D1709 | 120 | g | |
| 埃尔曼多夫抗撕强度 | MD: 38 µm, 吹塑薄膜 | ASTM D1922 | 61 | g | |
| TD: 38 µm, 吹塑薄膜 | ASTM D1922 | 650 | g | ||
| 热性能 | 熔点 | nan | ASTM D-2117 | 122 | ℃ |
| 维卡软化点 | nan | ASTM D-1525 | 101 | ℃ | |
| 脆化温度 | ASTM D-746 | <-70 | ℃ | ||
| 熔点 | DSC | 122 | ℃ | ||
| 软化点 | ASTM D-1525 | 93 | ℃ |