品名： LLDPE 牌号：1002 厂家：台达化学
规格用途| 规格级别 | 其它 薄膜 其它 | 外观颜色 | nan |
| 该料用途 | nan | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 密度 | nan | ASTM D-792 | 1.03 | nan |
| 吸水率 | nan | ASTM D-570 | 0.3 | WT% | |
| 熔体流动速率 | 200℃/5kg | nan | 2.6 | g/10min | |
| 密度 | nan | ISO 1183 | 1.06 | g/cm3 | |
| 熔体体积流率 | 220℃,10kg | ISO 1133 | 32 | g/10min | |
| 吸水率 | 23℃,24hr | ISO 62 | 0.30 | % | |
| 熔体流动速率 | 200℃/5.0kg | ASTM D-1238 | 3.5 | g/10min | |
| 熔体流动速率 | 200℃/5.0kg | ASTM D-1238 | 2.6 | g/10min | |
| 吸水率 | 24hr | ASTM D-570 | 0.30 | % | |
| 密度 | nan | ASTM D-1505 | 0.955 | g/cm3 | |
| 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 0.33 | g/10min | |
| 熔体流动速率 | 190℃/21.6kg | ASTM D-1238 | 29 | g/10min | |
| 热性能 | 热变形温度 | 未退火 | ASTM D-648 | 84 (183) | ℃(F) |
| 维卡软化点 | nan | ASTM D-1525 | 100 | ℃ | |
| 阻燃等级 | nan | UL94 | HB | nan | |
| 抗热线燃烧性 | nan | UL-746A | 16 | Sece | |
| 热变形温度 | nan | nan | 87 | ℃ | |
| 阻燃等级 | nan | UL94 | HB | nan | |
| 维卡软化温度 | B50 | ISO 306 | 103 | ℃ | |
| 燃烧性 | 1.50mm | UL 94 | HB | nan | |
| 热变形温度 | 1.80MPa，未退火，3.18mm | ASTM D-648 | 77.8 | ℃ | |
| 热变形温度 | 1.80MPa，退火，3.18mm | ASTM D-648 | 92.8 | ℃ | |
| 维卡软化温度 | nan | ASTM D-1525 | 104 | ℃ | |
| 阻燃性 | 1.59mm | UL 94 | HB | nan | |
| 热变形温度 | - | 66 psi， 未退火 | ASTM D648 | 199 | |
| 热变形温度 | - | 264 psi，未退火 | ASTM D648 | 193 | |
| 阻燃等级 | nan | UL 94 | HB | nan | |
| 热变形温度 | 1.80MPa，未退火，12.7mm | ASTM D-648 | 93.0 | ℃ | |
| CLTE | Flow | ASTM D-696 | 0.000080 | cm/cm/℃ | |
| 比热 | nan | ASTM C-351 | 1670 | J/kg/℃ | |
| 导热系数 | nan | ASTM C-177 | 0.21 | W/m.K | |
| 阻燃性 | NC | UL 94 | HB | nan | |
| 热变形温度 | 0.45MPa，未退火 | ASTM D-648 | 74.0 | ℃ | |
| 脆化温度 | nan | ASTM D-746 | -76.0 | ℃ | |
| 维卡软化温度 | nan | ASTM D-1525 | 128 | ℃ | |
| 熔化温度 | nan | DSC | 134 | ℃ | |
| 结晶温度 | nan | ASTM D-3418 | 111 | ℃ | |
| CLTE | nan | ASTM D-696 | 0.00013 | cm/cm/℃ |