规格用途
| 规格级别 |
其它 其它 其它 |
外观颜色 |
nan |
| 该料用途 |
nan |
| 备注说明 |
nan |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 机械性能 |
断裂伸长率 |
23℃ |
ASTM D-638 |
2< |
% |
| 热变形温度 |
1/4〃未退火 |
ASTM D-648 |
104-110 |
℃ |
| 挠曲模量 |
23℃ |
ASTM D-790 |
69000-75000 |
kg/cm2 |
| 拉伸强度 |
23℃ |
ASTM D-638 |
1100-1300 |
kg/cm2 |
| 洛氏硬度 |
23℃ |
ASTM D-785 |
121-127 |
R |
| 挠曲强度 |
23℃ |
ASTM D-790 |
1400-1600 |
kg/cm2 |
| IZOD冲击强度 |
23℃ 1/2"V凹口 |
ASTM D-256 |
4-7 |
kg.cm/cm |
| 拉伸强度 |
23℃ 50RH |
ASTM D-638 |
118 |
MPa |
| 断裂伸长率 |
nan |
ASTM D-638 |
3 |
MPa |
| 弯曲强度 |
23℃ 50RH |
ASTM D-790 |
150 |
MPa |
| 弯曲模量 |
23℃ 50RH |
ASTM D-790 |
7200 |
MPa |
| IZOD缺口冲击强度 |
23℃ 12.7mm |
ASTM D-256 |
39 |
J/m |
| 洛氏硬度 |
23℃ 50RH |
ASTM D-785 |
123 |
R-scale |
| 熔体流动速率 |
220℃/98N |
ISO 1133 |
13 |
g/10min |
| 热性能 |
热变形温度 |
1.82Mpa |
ASTM D-648 |
110 |
℃ |
| 球压痕温度 |
nan |
UL94 |
100 |
nan |
| 物理性能 |
熔体流动速率 |
240℃ 10kg |
ASTM D-1238 |
20-30 |
g/10min |
| 燃烧性 |
nan |
UL-94 |
94HB |
nan |
| 玻纤含量 |
650℃ 90分钟 |
nan |
18.5-21.5 |
% |
| 比重 |
23℃ |
ASTM D-792 |
1.20-1.24 |
nan |
| 吸水性 |
23℃×24小时 |
ASTM D-570 |
0.35> |
% |
| 比重 |
23℃ |
ASTM D-792 |
1.22 |
nan |
| 模具收缩率 |
nan |
nan |
0.1-0.3 |
% |