品名： EVA 牌号：720 厂家：韩国锦湖
规格用途| 规格级别 | 其它 其它 其它 | 外观颜色 | nan |
| 该料用途 | 用于HDPE/EVA、PP/EVA、LDPE/EVA、PVC和各种橡胶/EVA的热熔粘合和混合 | ||
| 备注说明 | VAC含量20% | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 熔体流动速率 | nan | nan | 150 | nan |
| 相对密度 | nan | nan | 0.947 | nan | |
| 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 18.0 | g/10min | |
| 密度 | 23℃ | ASTM D-792 | 1.04 | g/cm3 | |
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 2.0 | g/10min | |
| 熔体流动速率 | 200℃×21.6kg | ASTM D-1238 | 30 | g/10min | |
| 熔融指数 | 220℃,10kg | ISO 1133 | 6 | g/10min | |
| 吸水率 | nan | ISO 62 | 0.3 | % | |
| 密度 | nan | ISO 1183 | 1.05 | nan | |
| 密度 | nan | ASTM D-1505 | 0.947 | g/cm3 | |
| 熔体流动速率 | 220℃/10.0kg | ISO 1133 | 3.5 | g/10min | |
| 比重 | nan | ASTM D792 | 1.76 | g/cm3 | |
| 熔体流动速率 | nan | ASTM D1238 | 10 | g/10min | |
| 比重 | nan | ASTM D792 | 1.51 | g/cm3 | |
| 熔体流动速率 | nan | nan | 2.8 | g/10min | |
| 热性能 | 微卡软化点 | nan | ASTM D-1525 | 99(210) | °C（°F） |
| 热变形温度 | 6.4mm,18.6kg/cm2Annealed | ASTM D-648 | 97(206) | °C（°F） | |
| 热变形温度 | 6.4mm,18.6kg/cm2Unannealed | ASTM D-648 | 88(190) | °C（°F） | |
| 熔融指数 | 200°C,5kg(condition G) | ASTM D1238 | 2.5 | g/10min | |
| 熔融指数 | 200°C,21.6kg | 锦湖方法 | 30 | g/10min | |
| 热变形温度 | 6.4mm 18.6kg/cm2Annealed | ASTM D-648 | 97（206） | ℃（℉） | |
| 燃烧性 | nan | UL 94 | HB | CLASS | |
| 热变形温度 | 6.4mm 18.6kg/cm2Unannealed | ASTM D-648 | 88（190） | ℃（℉） | |
| 维卡软化点 | nan | ASTM D-1525 | 99（210） | ℃（℉） | |
| 热变形温度 | 1.80MPa,12.7mm | ISO 75/A | 77 | ℃ | |
| 热变形温度 | 1.82MPa,12.7mm | ASTM D-648 | 92 | ℃ | |
| 维卡软化点 | 50N,50℃/h | ISO 306/B50 | 86 | ℃ | |
| 维卡软化点 | 9.8N,50℃/h | ASTM D-1525 | 96 | ℃ | |
| 球压痕温度 | nan | nan | 90 | ℃ | |
| 线膨胀系数 | 流动方向 | ISO 11359 | 9 | ×10-5℃ | |
| 熔融温度 | nan | DSC | 69 | ℃ | |
| 热变形温度 | 0.45MPa，未退火 | ASTM D-648 | 96.0 | ℃ | |
| 燃烧性 | nan | UL 94 | HB | nan | |
| 阻燃等级 | nan | UL 94 | V-0 | nan | |
| 热变形温度 | 1.8 MPa, 未退火 | ISO 75 | 104 | ℃ | |
| 熔点 | ISO 3416C | 169 | ℃ | ||
| 阻燃等级 | UL 94 | V-0 |