品名： EVA 牌号：2010 厂家：意大利VAMP TECH
规格用途| 规格级别 | 其它 薄膜 其它 | 外观颜色 | nan |
| 该料用途 | 农业用宽幅薄膜，是加工性和机械物性优秀的产品 | ||
| 备注说明 | nan | ||
技术参数| 项目性能 | 性能子项 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
|---|---|---|---|---|---|
| 基本性能 | 熔体流动速率 | nan | ASTM D1238 | 0.4 | g/10min |
| 密度 | nan | ASTM D-1505 | 0.924 | g/cc | |
| 相对密度 | nan | ISO 1183 | 1.07 | g/cm3 | |
| 比重 | nan | ASTM D-792 | 1.34 | g/cm3 | |
| 密度 | nan | ISO 1043 | 1.24 | G/cm3 | |
| 比重 | ASTM D792 | 1.42 | g/cm³ | ||
| 成型收缩率 | Across flow | ISO 294-4 | 1.8 to 2.2 | % | |
| 吸水率 | ASTM D570 | 0.20 | % | ||
| 熔体质量流动速率 | ASTM D1238 | 1.7 | g/10 min | ||
| 熔体质量流动速率 | 190℃/2.16kg | ISO 1133 | 1.7 | g/10 min | |
| 成型收缩率 | flow | ASTM D955, ISO 294-4 | 1.8 to 2.2 | % | |
| 吸水率 | 24hr | ASTM D570 | 0.20 | % | |
| 洛氏硬度 | M-Scale | ASTM D785 | 94 | ||
| 洛氏硬度 | R-Scale | ASTM D785 | 120 | ||
| 熔体流动速率 | 230℃/2.16 kg | ASTM D1238 | 8-12 | g/10 min | |
| 热性能 | 维卡软化点 | nan | ASTM D-1525 | 92 | ℃ |
| 熔点 | nan | ASTM D-2117 | 107 | ℃ | |
| 熔融指数 | nan | ASTM D1238 | 1.7 | g/10min | |
| 线膨胀系数 | nan | nan | 10 | nan | |
| 热变形温度 | - | 0.45MPa | ASTM D648 | 172 | |
| 热变形温度 | - | 1.82MPa | ASTM D648 | 130 | |
| 阻燃性 | nan | UL94 | HB | nan | |
| 玻璃化转变温度 | nan | ASTM E1356 | 97.8 | ℃ | |
| 热畸变温度 | 0.45MPa,未退火 | ASTM D648 | 172 | °C | |
| 热畸变温度 | 1.8MPa,未退火 | ASTM D648 | 130 | °C | |
| 热畸变温度 | 0.45MPa,未退火 | ISO 75-2/B | 163 | °C | |
| 热畸变温度 | 1.8MPa,未退火 | ISO 75-2/A | 95.0 | °C | |
| 线性热膨胀系数 | flow | ASTM E831 | 0.00010 | cm/cm/°C | |
| 热变形温度 | 0.45MPA，未退火 | ASTM D648 | 102 | ℃ | |
| 热变形温度 | 1.8 MPa, 未退火 | ASTM D648, ISO 75-2/A | 140 | ℃ | |
| 维卡软化点 | ISO 306/B, ASTM D1525 | 120 | ℃ | ||
| 阻燃等级 | 0.800mm | UL 94 | HB | ||
| 阻燃等级 | 1.60mm | UL 94 | HB | ||
| 阻燃等级 | 3.20mm | UL 94 | HB | ||
| 最高连续使用温度 | Internal Method | 140 | ℃ | ||
| Service Temperature | IEC 60216 | 100 | ℃ | ||
| 维卡软化温度 | ISO 306/B,ASTM D1525 | 128 | ℃ | ||
| 球压试验 | 125 ℃ | IEC 60695-10-2 | Pass | ||
| 工作温度 | IEC 60216 | 120 | ℃ | ||
| UL 阻燃等级 | 0.800 mm | UL 94 | HB | ||
| UL 阻燃等级 | 1.60 mm | UL 94 | HB | ||
| UL 阻燃等级 | 3.20 mm | UL 94 | HB | ||
| 极限氧指数 | ASTM D2863,ISO 4589-2 | 25 | % | ||
| 最高连续使用温度 | Internal Method | 180 | ℃ | ||
| 维卡软化温度 | ISO 306/B, ASTM D1525 2 | 207 | ℃ | ||
| Ball Pressure Test | 125℃ | IEC 60695-10-2 | pass | ||
| 165℃ | IEC 60695-10-2 | pass | |||
| Service Temperature | IEC 60216 | 130 | ℃ | ||
| 热性能 | 最高连续使用温度 | 180 | |||
| 维卡软化温度 | ISO 306/B, ASTM D1525 | 247 | °C | ||
| Ball Pressure Test | 125°C | IEC 60695-10-2 | Pass | ||
| 165°C | IEC 60695-10-2 | Pass | |||
| Service Temperature | IEC 60216 | 130 | °C |