规格用途
| 规格级别 |
其它 薄膜 其它 |
外观颜色 |
nan |
| 该料用途 |
适合一般用的包装薄膜和微薄薄膜 |
| 备注说明 |
特性：光学性优异，有广泛的加工性能 |
技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| |
熔流率 |
(250°C/3.8 kg) |
ASTM D1238 |
25 |
g/10 min |
| 收缩率-流动 |
|
ASTM D955 |
0.0070 到 0.012 |
in/in |
| 吸水率 |
(73°F, 24 hr) |
ASTM D570 |
0.15 |
% |
| 伸长率 (断裂) |
|
ASTM D638 |
50 |
% |
| 弯曲模量 |
|
ASTM D790 |
284000 |
psi |
| 弯曲强度 (屈服) |
|
ASTM D790 |
11400 |
psi |
| |
264 psi, 未退火 |
ASTM D648 |
171 |
°F |
| 线形膨胀系数 - 流动 |
|
ASTM D696 |
0.000046 |
in/in/°F |
| 介电强度 |
|
ASTM D149 |
580 |
V/mil |
| 介电常数 |
|
ASTM D150 |
3.00 |
|
| 耗散因数 |
|
ASTM D150 |
0.0090 |
|
| 耐电弧性 |
|
ASTM D495 |
118 |
sec |
| 基本性能 |
相对密度 |
nan |
nan |
0.921 |
nan |
| 熔体流动速率 |
nan |
nan |
4 |
nan |
| 比重 |
nan |
ASTM D-792 |
1.50 |
nan |
| 熔融指数 |
nan |
JIS K-7210 |
25 |
g/10min |
| 热性能 |
阻燃等级 |
nan |
UL 94 |
V-0 |
nan |
| 软化点 |
nan |
ASTM D-1525 |
105 |
℃ |
| 热变形温度 |
nan |
ASTM D-648 |
88 |
℃ |
| 热变形温度 |
1.8MPa，未退火 |
ASTM D648 |
85.0 |
℃ |
| 阻燃等级 |
0.630 mm |
UL 94 |
V-0 |
|
| 熔融温度 |
|
|
260 |
℃ |
| 热变形温度 |
0.45MPa,未退火 |
ASTM D648 |
158 |
℃ |
| 热变形温度 |
1.8MPa,未退火 |
ASTM D648 |
110 |
℃ |
| UL阻燃等级 |
0.800mm |
UL 94 |
HB |
|
| 熔融温度 |
|
ASTM D648 |
166 |
℃ |
| 热变形温度 |
66 psi, 未退火 |
ASTM D648 |
/ |
°F |