技术参数
| 项目性能 |
性能子项 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
nan |
ASTM-D792 |
1.05 |
nan |
| 密度 |
nan |
ISO 1183 |
1.05 |
g/cm3 |
| 熔体流动速率 |
220℃/10.0kg |
ISO 1133 |
18.0 |
cm3/10min |
| 熔体流动速率 |
220℃/10.0kg |
ASTM D-1238 |
19 |
g/10min |
| 熔体流动速率 |
230℃/3.8kg |
ASTM D-1238 |
5.0 |
g/10min |
| 吸水率 |
24hr |
ASTM D-570 |
0.25 |
% |
| 热性能 |
UL长期使用温度（含冲击） |
nan |
nan |
60 |
℃ |
| 热变形温度 |
1.8MPa |
ASTM D-648 |
92 |
℃ |
| 热变形温度 |
nan |
ASTM-D648 |
88 |
℃ |
| 热变形温度 |
1.80MPa，未退火 |
ISO 75-2/Af |
79.0 |
℃ |
| CLTE |
Flow |
ISO 11359-2 |
0.000090 |
cm/cm/℃ |
| 阻燃性 |
1.50mm |
UL 94 |
HB |
nan |
| 热变形温度 |
1.80MPa，未退火，3.20mm |
ASTM D-648 |
77.0 |
℃ |
| 热变形温度 |
1.80MPa，未退火，6.40mm |
ASTM D-648 |
83.0 |
℃ |
| 热变形温度 |
1.80MPa，未退火，12.7mm |
ASTM D-648 |
88.0 |
℃ |
| 维卡软化温度 |
nan |
ASTM D-1525 |
102 |
℃ |
| CLTE |
Flow |
ASTM D-696 |
0.000090 |
cm/cm/℃ |
| 燃烧性 |
1.60mm |
UL 94 |
HB |
nan |
| 热稳定性 |
|
CEI 20-34/3-2 |
> 1 |
hr |
| 冷挠曲性 |
|
ISO 458/2 |
-60 |
℃ |
| 冷挠曲性 |
|
ISO 458/2 |
-60 |
℃ |
| 冷挠曲性 |
|
ISO 458/2 |
-55 |
℃ |
| 冷挠曲性 |
|
ISO 458/2 |
-30 |
℃ |
| 冷挠曲性 |
|
ISO 458/2 |
-35 |
℃ |
| 冷挠曲性 |
|
ISO 458/2 |
-35 |
℃ |
| 冷挠曲性 |
|
ISO 458/2 |
-30 |
℃ |
| 冷挠曲性 |
|
ISO 458/2 |
-25 |
℃ |
| 热变形温度 |
1.82MPa |
GB 1634 |
245 |
℃ |
| 热变形温度 |
0.45 MPa, 未退火, 6.35 mm |
ASTM D648 |
141 |
℃ |
| |
1.8 MPa, 未退火, 6.35 mm |
ASTM D648 |
135 |
℃ |
| 线形膨胀系数 - 流动 |
6.35 mm |
ASTM D696 |
0.000068 |
cm/cm/℃ |
| 比热 |
|
ASTM C351 |
1260 |
J/kg/℃ |
| 导热系数 |
|
ASTM C177 |
0.19 |
W/m/K |
| 光学性能 |
折射率 |
|
ASTM D542 |
1.490 |
|
| 透光度 |
|
ASTM D1003 |
92.0 |
% |
| 雾度 |
|
ASTM D1003 |
1.5 |
% |